The redistribution of solutes during steel solidification induces macrosegregation ultimately.
摘要
钢凝
溶质再分配是产生宏观偏析根本原因。
The redistribution of solutes during steel solidification induces macrosegregation ultimately.
摘要钢凝溶质再分配是产生宏观偏析根本原因。
The reason of gas-hole defects occured in steel casting for molding eroduction line was analyzed.
结合多年生产实践,分析了湿型砂水平造型生产线上钢件产生气孔原因,介绍了预防钢件气孔措施。
The foundation bolt of conticaster steel ladle revolving table is the most critical part to the equipment.
连钢包回转台地脚螺栓,是设备上最为关
位。