It holds that main causes promoting crack on martensite stainless steel are gross martensite and crystal boundary carburet and secondary phase distributed along crystal boundary.
文章认为，粗大
马氏体组织、晶界碳化物以及沿晶界分布“第二相”组织是促使马氏体不锈钢产生
主要原因。
It holds that main causes promoting crack on martensite stainless steel are gross martensite and crystal boundary carburet and secondary phase distributed along crystal boundary.
文章认为，粗大马氏体组织、晶界碳化物以及沿晶界分布“第二相”组织是促使马氏体不锈钢产生主要原因。
The crack initiates at stress concentration point in the root of weld, where has much more martenite, carbide and inclusion, and the serious hydrogen segregation.
均在焊缝根部应力集中
萌生，该马氏体含量比较大，碳化物及夹杂物较多，氢偏
严重。
The high wearing resistance of the samples after hydrocooling and air cooling was partially attributed to martensite transformation and work-hardening.
经水冷和空冷试样具有高耐磨性重要原因是其在磨损过程中诱发了马氏体相变,出加工硬化。
The structural parameter for austenitic phasetransformation has a great effect on the characteristic of martensitic transformation.
发奥氏体相变结构参数对马氏体相变特性有很大影响。